Innova R 830D

Category:	PS (HIPS) , High Impact Polystyrene
Manufacturer:	Innova SA
Trademark:	Innova
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GSprMT_Innova-R-830D.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Characteristics:

High stress cracking resistance (ESCR)

Good mechanical properties and imact resistance

Process:

Extrusion and thermoforming

Injection moulding

Applications:

Refrigeration (refrigerator doors and inner liner)

Fatty foods packaging (eg margarine)

General Information
Features	Food Contact Acceptable High ESCR (Stress Crack Resist.) High Impact Resistance
Uses	Consumer Applications Food Packaging Non-specific Food Applications Packaging
Agency Ratings	FDA 21 CFR 177.1640
Forms	Pellets
Processing Method	Extrusion Injection Molding Thermoforming

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.04	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) (200°C/5.0 kg)	3.0	g/10 min	ASTM D1238, ISO 1133
Molding Shrinkage	0.40 to 0.70	%	ISO 294-4
Water Absorption
Saturation	< 0.10	%	ASTM D570
Saturation, 23°C	< 0.10	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (L-Scale)	51		ASTM D785, ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	1450	MPa	ASTM D638, ISO 527-2
Tensile Strength
Break, 23°C	23.0	MPa	ASTM D638
Break, 23°C	24.0	MPa	ISO 527-2
Tensile Elongation
Break, 23°C	60	%	ASTM D638
Break, 23°C	65	%	ISO 527-2
Flexural Strength
23°C	36.0	MPa	ASTM D790
23°C	34.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact
23°C, 3.20 mm	140	J/m	ASTM D256
23°C	11	kJ/m²	ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	84.0	°C	ASTM D648, ISO 75-2/A
Vicat Softening Temperature
--	98.0	°C	ASTM D1525, ISO 306/A50 2 ¹
--	88.0	°C	ASTM D1525, ISO 306/B50 3 ²

Flammability	Nominal Value		Test Method
Flame Rating (1.60 mm)	HB		UL 94

Injection	Nominal Value	Unit
Processing (Melt) Temp	210 to 260	°C
Mold Temperature	40.0 to 75.0	°C

Extrusion	Nominal Value	Unit
Melt Temperature	210 to 240	°C

Note Message
1 .	Rate A (50°C/h), Loading 1 (10 N)
2 .	Rate A (50°C/h), Loading 2 (50 N)

Resin Grade	Manufacturer	Category	Trademark
SKYGREEN® K2012	SK Chemicals	PETG	SKYGREEN®
Trademark PP PPH1200MA	Trademark Plastics Corporation	PP Homopolymer	Trademark PP
Grilamid® TRVX-50X9 nat	EMS-GRIVORY	Nylon 12	Grilamid®
Panlite® MN-3600H	TEIJIN LIMITED	PC Alloy	Panlite®
TECHNYL® C 216 V45 NATURAL	Solvay Engineering Plastics	Nylon 6	TECHNYL®