Trithene® CX 7065
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Trithene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSgiZI_Trithene-CX-7065.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trithene®CX 7065 is a low density polyethylene material,. This product is available in Latin America and is processed by extrusion coating. Trithene®The main characteristics of CX 7065 are: contact with food. Typical application areas include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.918 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.5 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 9.50 | MPa | ASTM D638 |
| Fracture, molding | 8.50 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 300 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 50 µm, blown film | 87.0 | MPa | ASTM D882 |
| 5% secant, TD : 50 µm, blown film | 95.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 16.0 | MPa | ASTM D882 |
| TD : Broken, 50 µm, blown film | 14.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 50 µm, blown film | 300 | % | ASTM D882 |
| TD : Broken, 50 µm, blown film | 350 | % | ASTM D882 |
| Dart Drop Impact (50 µm, Blown Film) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, blown film | 370 | g | ASTM D1922 |
| TD : 50 µm, blown film | 240 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 83.0 | °C | ASTM D1525 |
| Melting Temperature | 110 | °C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 50.0 µm, Blown Film) | 68 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 12 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 50 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 5.8 to 7.2 g/10 minDensity, ASTM D1505: 0.916 to 0.920 g/cm³ |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 190 - 210 | °C | |
| Cylinder Zone 2 Temp. | 220 - 270 | °C | |
| Cylinder Zone 3 Temp. | 260 - 330 | °C | |
| Adapter Temperature | 290 - 330 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIBUR Synthetic Rubber SBR-1712 HI-AR Grade A | SIBUR, LLC | SBR, Unspecified | SIBUR Synthetic Rubber |
| Tisblend® PC-ABS UNR | Tisan | PC+ABS | Tisblend® |
| Ultramid® A3SK | BASF Corporation | Nylon 66 | Ultramid® |
| DIC.PPS FZ-3600-R5 | DIC Corporation | PPS | DIC.PPS |
| Moplen HP6057 | LyondellBasell Industries | PP Homopolymer | Moplen |