LNP™ LUBRICOMP™ KCL34A compound
| Category: | Acetal (POM) Homopolymer , Acetal (POM) Homopolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSg20H_LNPLUBRICOMPKCL34Acompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP KCL34A is a compound based on Acetal Homopolymer resin containing PTFE, Carbon Fiber. Added features of this material include: Internally Lubricated, Electrically Conductive. Also known as: LNP* LUBRICOMP* Compound KCL-4034 D Product reorder name: KCL34A |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.56 | g/cm³ | ASTM D792 |
| -- | 1.55 | g/cm³ | ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.70 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.3 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.3 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.73 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 17200 | MPa | ASTM D638 |
| -- | 15500 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 87.6 | MPa | ASTM D638 |
| Yield | 88.0 | MPa | ISO 527-2 |
| Fracture | 87.6 | MPa | ASTM D638 |
| Fracture | 88.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 0.70 | % | ASTM D638 |
| Yield | 0.73 | % | ISO 527-2 |
| Fracture | 0.70 | % | ASTM D638 |
| Fracture | 0.72 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 13100 | MPa | ASTM D790 |
| -- | 15000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 110 | MPa | ASTM D790 |
| -- | 117 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.35 | ASTM D3702 Modified | |
| With Self-Static | 0.32 | ASTM D3702 Modified | |
| Wear Factor - Washer | 69.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 2 | 3.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 270 | J/m | ASTM D4812 |
| 23°C 3 | 17 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.40 | J | ASTM D3763 |
| -- | 1.90 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 175 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 175 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 171 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 170 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.6E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 2.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DJSilicone NE-Z150 | DONGJUE SILICONE (NANJING) CO., LTD | Silicone | DJSilicone |
| ESPOLEX WT361 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |
| Latilub 66-15T K/30 | LATI S.p.A. | Nylon 66 | Latilub |
| SQUARE® LSG6931-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |
| Sylvin 86049-50 Clear 876 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |