InnoPlus HD6376EB
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | PTT Global Chemical Public Company Limited |
| Trademark: | InnoPlus |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GSblCG_InnoPlus-HD6376EB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
InnoPlus HD6376EB is black compounded high density polyethylene extrusion grade for cable jacket like fiber optic. This grade provide excellent UV and weathering resistance, abrasion resistance and low shrink back. Material Specification : Black compounded InnoPlus HD6376EB meet the following requirement of
Typical Application: Cable jackets |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | ASTM D1505 | ||
| Base Resin | 0.952 | g/cm³ | |
| Black | 0.962 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.060 | g/10 min | |
| 190°C/5.0 kg | 0.30 | g/10 min | |
| Environmental Stress-Cracking Resistance (25% Igepal, F50) | > 2000 | hr | ASTM D1693B |
| Carbon Black Content | 2.5 | % | ASTM D4218 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 63 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 22.6 | MPa | |
| Break | 32.4 | MPa | |
| Tensile Elongation (Break) | 750 | % | ASTM D638 |
| Apparent Bending Modulus | 785 | MPa | ASTM D747 |
| Flexural Modulus | 981 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 1 | 390 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 122 | °C | ASTM D1525 2 |
| Melting Temperature | 129 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 3 | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Constant (1 MHz) | 2.50 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 5.0E-3 | ASTM D150 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Track Resistance | Pass | IEEE 1222 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 220 | °C | |
| Cylinder Zone 2 Temp. | 180 to 220 | °C | |
| Cylinder Zone 3 Temp. | 180 to 220 | °C | |
| Cylinder Zone 4 Temp. | 180 to 220 | °C | |
| Cylinder Zone 5 Temp. | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | Non break |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | DC 500V |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pro-fax PH350 | LyondellBasell Industries | PP Homopolymer | Pro-fax |
| ALCUDIA® EVA PA-443 | REPSOL | EVA | ALCUDIA® EVA |
| Gallonprene® GP520-9005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| HiFill® PA6 0254 C | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| TOTAL Polyethylene HD 6082 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |