Innothane® IE-5000
| Category: | TSU , Polyurethane Thermoset Elastomer |
| Manufacturer: | Innovative Polymers, Inc. |
| Trademark: | Innothane® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GS1QGI_Innothane-IE-5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| IE-5000 is a soft, abrasion resistant elastomer formulated for room temperature hand-batch processing. The unique chemistry of the system imparts excellent electrical properties, hydrolytic stability, and flexibility at low temperatures. Excellent physical properties can be obtained without the utilization of mercury, MOCA, or TDI. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Specific Gravity | |||
| Hardener | 1.00 | g/cm³ | |
| Base Resin | 1.11 | g/cm³ |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.8E+16 | ohms | ASTM D270 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Volume: 100 Mix Ratio by Weight: 100 | ||
| Resin | Mix Ratio by Weight: 100 Mix Ratio by Volume: 90 | ||
| Demold Time | 300 to 420 | min |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Viscosity | |||
| 25°C 1 | 0.050 | Pa·s | |
| 25°C 2 | 1.2 | Pa·s | |
| 25°C 3 | 4.8 | Pa·s | |
| Curing Time 4 | 40 | hr | |
| Gel Time | 15 to 25 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 35 to 45 | ASTM D2240 | |
| Tensile Strength | 2.76 | MPa | ASTM D638 |
| Tensile Elongation at Break | 200 | % | ASTM D638 |
| Tear Strength | 13.1 | kN/m | ASTM D624 |
| Electric Strength (25°C) | 22 | kV/mm | ASTM D149 |
| Relative Permittivity (25°C) | 2.50 | ASTM D150 | |
| Volume Resistivity | 2.0E+16 | ohms·cm | ASTM D270 |
| Dissipation Factor (1 kHz, 25°C) | 0.015 | ASTM D150 |
| Note Message | |
|---|---|
| 1 . | Resin |
| 2 . | Mixed |
| 3 . | Hardener |
| 4 . | 24 hours at 77°F + 16 hours at 160°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ A70 G14 TM-X NC060 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| EvoSource™ ABS 4136 70/35 | MBA Polymers | ABS | EvoSource™ |
| HiFill® PA6/6 LGF60 HS L BK 12mm | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| PIVINEL™ VFR-5013 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |
| SQUARE® SCR2524-70A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |