KOPLA PA6 KNG1030
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | KOPLA Co., Ltd. |
| Trademark: | KOPLA PA6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GRBRgY_KOPLA-PA6-KNG1030.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KOPLA PA6 KNG1030 is a Polyamide 6 (Nylon 6) material filled with glass fiber. It is available in Asia Pacific. Primary attribute of KOPLA PA6 KNG1030: Flame Rated. Typical application of KOPLA PA6 KNG1030: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.90 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 1.3 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 172 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.0 | % | ASTM D638 |
| Flexural Modulus (23°C) | 7750 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 226 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 215 | °C | |
| 1.8 MPa, Unannealed | 208 | °C | |
| Melting Temperature | 220 | °C | |
| CLTE - Flow | 3.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Trademark PP PPC5020MA | Trademark Plastics Corporation | PP Impact Copolymer | Trademark PP |
| ALTECH® PA66 B 2030/507 GF30 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| Braskem PP TI4450M | Braskem America Inc. | PP Impact Copolymer | Braskem PP |
| CP PRYME® Polystyrene PS100-8M NAT | Chase Plastics Services Inc. | PS (GPPS) | CP PRYME® Polystyrene |
| LEXAN™ 923X resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |