| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Soredi S.p.a. |
| Trademark: | Niretan A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GQmEgU_Niretan-A-AE-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 66 flame retardant with an UL 94 V0 at 1.6 mm rating |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.16 | -- | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 8.0 | 9.0 | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | 3.1 | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | 85 | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength 1(Yield) | 85.0 | 45.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 3000 | 1500 | MPa | ASTM D790 |
| Flexural Strength 3(Break) | 140 | 170 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| 0°C, 3.20 mm | 30 | 80 | J/m | |
| 23°C, 3.20 mm | 40 | 200 | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | -- | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 256 | -- | °C | ASTM D3418 |
| CLTE - Flow | 3.0E-6 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 90 | 50 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | 5.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.014 | 0.016 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | V-0 | -- | ||
| 3.20 mm | V-0 | -- | ||
| Glow Wire Ignition Temperature (2.00 mm) | 960 | -- | °C | IEC 60695-2-13 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultracast II TC-1630 A/B | BJB Enterprises, Inc. | TSU | Ultracast II |
| Celanex® 4022 | Celanese Corporation | PBT | Celanex® |
| Durethan® BG 30 X H2.0 XF 901510 | LANXESS GmbH | Nylon 6 | Durethan® |
| Guardian III™ PJ | S&E Specialty Polymers, LLC | PVC, Unspecified | Guardian III™ |
| Kepital® GD-52 | Korea Engineering Plastics Co., Ltd | Acetal (POM) Copolymer | Kepital® |