Nucrel® 0908HS
| Category: | EMAA , Ethylene Methacrylic Acid |
| Manufacturer: | DuPont Packaging & Industrial Polymers |
| Trademark: | Nucrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GQfqWu_Nucrel-0908HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nucrel® 0908HS is an ethylene-methacrylic acid copolymer resin, made with nominally 9 wt% methacrylic acid. The resin is available for use in conventional extrusion coating, coextrusion coating, and cast film operations designed to process polyethylene resins. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.930 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238, ISO 1133 |
| Methacrylic Acid Content | 9.2 | wt% |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Freezing Point | 82 | °C | ASTM D3418 |
| Vicat Softening Temperature | 80.0 | °C | ASTM D1525, ISO 306 |
| Peak Melting Temperature | 100 | °C | ASTM D3418, ISO 3146 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 185 | °C | |
| Cylinder Zone 2 Temp. | 235 | °C | |
| Cylinder Zone 3 Temp. | 260 | °C | |
| Cylinder Zone 4 Temp. | 285 | °C | |
| Cylinder Zone 5 Temp. | 285 | °C | |
| Adapter Temperature | 285 | °C | |
| Melt Temperature | 260 to 310 | °C | |
| Die Temperature | 285 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® A RV350LW 333 NER 4815 | Radici Plastics | Nylon 66 | Radilon® |
| Sarlink® TPE EE-2272B BLK | Teknor Apex Company | TPE | Sarlink® TPE |
| Shuang-Bang CM-0155H | Shuang-Bang Industrial Corp. | Film, TPU | Shuang-Bang |
| Caltex PP H240M | GS Caltex | PP Homopolymer | Caltex PP |
| ESENTTIA 130C80ND | Polipropileno del Caribe S.A. | PP Impact Copolymer | ESENTTIA |