Geon™ HTX E1502
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GPBWr3_Geon-HTX-E1502.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VSI FLAMMABILITY:Burn Length (0.040 in Bar)ASTM D635 0* IN.Burn Time (0.040 in Bar) ASTM D635 0* Sec.*Extinguished before 25 MM starting ref mark. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 11445 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 79 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2740 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 49.6 | MPa | ASTM D638 |
| Flexural Modulus | 2770 | MPa | ASTM D790 |
| Flexural Strength | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 34 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 67.6 | J/cm | |
| 23°C 4 | 68.9 | J/cm |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed, 3.18 mm 5 | 88.9 | °C | ASTM D648 |
| 0.45 MPa, Annealed, 3.18 mm 6 | 90.0 | °C | ASTM D648 |
| 1.8 MPa, Annealed, 3.18 mm 7 | 84.4 | °C | ASTM D648 |
| CLTE - Flow | 6.4E-5 | cm/cm/°C | ASTM D696 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 193 to 204 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 5.1 mm/min |
| 2 . | Type I, 5.1 mm/min |
| 3 . | Procedure A, C.125 Dart |
| 4 . | Procedure B, C.125 Dart |
| 5 . | Annealed at 50 deg.C |
| 6 . | Annealed at 60 deg.C |
| 7 . | Annealed at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® H511-03 | Safripol (PTY) LTD | PP Homopolymer | Safron® |
| Flexane® Brushable | Devcon | PUR, Unspecified | Flexane® |
| Hylex® P1317FRMA | Ravago Manufacturing Americas, LLC | PC | Hylex® |
| INELEC PA66CF20 | Infinity LTL Engineered Compounds | Nylon 66 | INELEC |
| Karina BLACK PVC COMPOUND 650-48/ 1-E | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |