DOWLEX™ NG 2432.10 UE
| Category: | LLDPE , Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOWLEX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GP0LYS_DOWLEX-NG-2432-10-UE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DOWLEX™ NG 2432 UE Polyethylene Resin for rotational and injection moulding from Dow Plastics is specifically designed for applications requiring stiffness in combination with excellent mechanical properties and good processing. The powder version is named DOWLEX™ NG 2432.10 UE Polyethylene Resin. Processing and Stabilization: DOWLEX™ NG 2432 UE Polyethylene Resin is fully heat and UV-stabilised resulting in a wide processing latitude, good colour retention and long life expectancy. Note: DOWLEX™ NG 2432 UE Polyethylene Resin should comply with FDA regulation 177.1520 and with most European food contact regulations when used unmodified and processed according to good manufacturing practices for food contact applications. Applications:
|
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.939 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.8 | g/10 min | ISO 1133 |
| Environmental Stress-Cracking Resistance | ASTM D1693 | ||
| 50°C, 10% Antarox, Compression Molded | 70.0 | hr | |
| 50°C, 100% Antarox, Compression Molded | > 1000 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, Compression Molded) | 59 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield, Compression Molded | 19.0 | MPa | |
| Yield, Rotational Molded 1 | 18.0 | MPa | |
| Break, Compression Molded | 9.70 | MPa | |
| Break, Rotational Molded 2 | 8.10 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Break, Compression Molded | 550 | % | |
| Break, Rotational Molded 3 | 500 | % | |
| Flexural Modulus - 1% Secant (Compression Molded) | 730 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | ||
| -20°C, Rotational Molded 4 | 69.0 to 92.0 | J | |
| -20°C, 1.00 mm, Compression Molded | 24.0 | J | |
| 23°C, Rotational Molded 5 | 45.0 to 60.0 | J | |
| 23°C, 1.00 mm, Compression Molded | 15.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 65.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 123 | °C | ISO 306/A120 |
| Melting Temperature | 128 | °C | DSC |
| Peak Crystallization Temperature (DSC) | 106 | °C | DSC |
| Note Message | |
|---|---|
| 1 . | 3 to 4 mm plate thickness |
| 2 . | 3 to 4 mm plate thickness |
| 3 . | 3 to 4 mm plate thickness |
| 4 . | 3 to 4 mm plate thickness |
| 5 . | 3 to 4 mm plate thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiten® 112 | ITEN INDUSTRIES | Phenolic | Resiten® |
| Trademark PE LLB1918F | Trademark Plastics Corporation | LLDPE | Trademark PE |
| Delrin® FG150 NC010 | DuPont Performance Polymers | Acetal (POM) Homopolymer | Delrin® |
| Karina COMP. PVC NATURAL -E 600-DA-35/ 1-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| RTP 199 X 135936 B | RTP Company | PP, Unspecified | RTP |