POCAN® BF 4222 000000

Category:	PBT , Polybutylene Terephthalate
Manufacturer:	LANXESS Corporation
Trademark:	POCAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GONY8Q_POCANBF4222000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PBT, 20 % glass fibers, injection molding, flame retardant

General Information
Filler / Reinforcement	Glass fiber reinforced material, 20% filler by weight
Additive	Flame retardancy
Features	Flame retardancy
Agency Ratings	EC 1907/2006 (REACH)
Processing Method	Injection molding
Resin ID (ISO 1043)	PBT GF FR (17)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.57	g/cm³	ISO 1183
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)	12.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 2577
Vertical flow direction : 260°C, 2.00mm ¹	1.1	%	ISO 2577
Vertical flow direction : 120°C, 4 hours, 2.00mm ²	0.20	%	ISO 2577
Flow direction : 260°C, 2.00mm ³	0.50	%	ISO 2577
Flow direction : 120°C, 4 hours, 2.00mm ⁴	0.20	%	ISO 2577
Water Absorption			ISO 62
Saturated, 23°C	0.40	%	ISO 62
Equilibrium, 23°C, 50% RH	0.20	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	176	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	7500	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	115	MPa	ISO 527-2/5
Flexural Modulus ⁵(23°C)	7900	MPa	ISO 178/A
Flexural Stress ⁶(23°C)	190	MPa	ISO 178/A
Flexural Strain at Flexural Strength ⁷(23°C)	3.3	%	ISO 178/A

Additional Information	Nominal Value		Test Method
ISO Shortname	PBT, GFHMR, 09-070, GF20		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 - 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	< 10	kJ/m²	ISO 179/1eA
23°C	< 10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	45	kJ/m²	ISO 179/1eU
23°C	50	kJ/m²	ISO 179/1eU
Notched Izod Impact			ISO 180/1A
-30°C	< 10	kJ/m²	ISO 180/1A
23°C	< 10	kJ/m²	ISO 180/1A
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	40	kJ/m²	ISO 180/1U
23°C	45	kJ/m²	ISO 180/1U

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	215	°C	ISO 75-2/B
1.8 MPa, not annealed	195	°C	ISO 75-2/A
Vicat Softening Temperature	211	°C	ISO 306/B50
Ball Pressure Test (211°C)	Pass		IEC 60695-10-2
Melting Temperature ⁸	222	°C	ISO 11357-3
Linear thermal expansion coefficient			ISO 11359-2
Flow : 23 to 55°C	3.0E-5	cm/cm/°C	ISO 11359-2
Lateral : 23 to 55°C	1.0E-4	cm/cm/°C	ISO 11359-2

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+17	ohms	IEC 60093
Volume Resistivity (23°C)	> 1.0E+16	ohms·cm	IEC 60093
Dielectric Strength (23°C, 1.00 mm)	31	kV/mm	IEC 60243-1
Comparative Tracking Index (CTI)	PLC 2		UL 746
Comparative Tracking Index (Solution A)	225	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.750 mm	V-0		UL 94
1.50 mm	V-0		UL 94
3.00 mm	V-0		UL 94
Glow Wire Flammability Index			IEC 60695-2-12
0.750 mm	960	°C	IEC 60695-2-12
1.50 mm	960	°C	IEC 60695-2-12
3.00 mm	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature			IEC 60695-2-13
0.750 mm	800	°C	IEC 60695-2-13
1.50 mm	800	°C	IEC 60695-2-13
3.00 mm	800	°C	IEC 60695-2-13
Oxygen Index ⁹	29	%	ISO 4589-2

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Dry Air Dryer	120	°C
Drying Time - Dry Air Dryer	4.0 - 8.0	hr
Processing (Melt) Temp	240 - 260	°C
Mold Temperature	80.0 - 100	°C

Note Message
1 .	60x60x2mm, 80°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 80°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min
9 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
Zenite® ZE88410NXL	Celanese Corporation	LCP	Zenite®
Kynar Flex® 2750-01	Arkema	PVDF	Kynar Flex®
Lucene™ LC370	LG Chem Ltd.	TPO (POE)	Lucene™
Plenco 02000 (Compression)	Plastics Engineering Co.	Phenolic	Plenco
KOPPS® S38A65BL	Kolon Plastics, Inc.	PPS	KOPPS®