LEXAN™ 3412HF resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GO4aQo_LEXAN3412HFresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 20% glass reinforced, high flow PC. UL rated V-1 at 0.059", |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 8.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.20 - 0.40 | % | Internal method |
| Transverse flow : 3.20mm | 0.45 - 0.65 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3450 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 100 | MPa | ASTM D638 |
| Fracture | 107 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 5520 | MPa | ASTM D790 |
| Flexural Strength 5 | ASTM D790 | ||
| Yield, 50.0mm span | 157 | MPa | ASTM D790 |
| Fracture, 50.0mm span | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 110 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 3.39 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 142 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 3.00 mm | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ColorRx® TPE-OM50A0RXTL | LTL Color Compounders, Inc. | TPE | ColorRx® |
| ExxonMobil™ LDPE LD 331.08 | ExxonMobil Chemical | LDPE | ExxonMobil™ LDPE |
| Hifax TYC 900P | LyondellBasell Industries | PP Impact Copolymer | Hifax |
| OXNILON 6 33GF | Oxford Polymers | Nylon 6 | OXNILON 6 |
| Eastalloy DA003-8999K | Eastman Chemical Company | PC+Polyester | Eastalloy |