DENKA Transparent Polymer TX-800LF
| Category: | MMS , Methyl Methacrylate Styrene |
| Manufacturer: | Denka Company Limited |
| Trademark: | DENKA Transparent Polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GO2z5T_DENKA-Transparent-Polymer-TX-800LF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DENKA Transparent Polymer TX-800LF is a Methyl Methacrylate Styrene (MMS) product. It can be processed by injection molding and is available in Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.11 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 1.6 | g/10 min | ISO 1133 |
| Molding Shrinkage (2.00 mm) | 0.40 | % | Internal Method |
| Water Absorption (Equilibrium) | 0.090 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 64.0 | MPa | ISO 527-2/5 |
| Nominal Tensile Strain at Break | 5.0 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3400 | MPa | ISO 178 |
| Flexural Stress 2 | 113 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 79.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 100 | °C | ISO 306/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index 3 | 1.550 | ASTM D542 | |
| Transmittance (2000 µm) | 92.0 | % | ISO 13468-1 |
| Haze (2000 µm) | 0.20 | % | ISO 14782 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 190 to 240 | °C | |
| Middle Temperature | 190 to 240 | °C | |
| Front Temperature | 190 to 240 | °C | |
| Nozzle Temperature | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | NA*D ray |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RONFALIN® C C110FR | A. Schulman Europe | PC+ABS | RONFALIN® C |
| YUNTIANHUA® M25 | YunNan YunTianHua Co., Ltd. | Acetal (POM) Copolymer | YUNTIANHUA® |
| Calsak ABS CS-72 | Calsak Polymers | ABS | Calsak ABS |
| DURACON® M90-44 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | DURACON® |
| PIVINEL™ 122-RDV-LF | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |