VENYL SW107 - 7727
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GNrNkR_VENYL-SW107---7727.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL SW107 - 7727 is a Polyamide 6 (Nylon 6) product filled with 15% glass bead. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.2 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.5 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3500 | 1150 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 80.0 | 52.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 30 | 120 | % | ISO 527-2 |
| Flexural Modulus | 3150 | 1000 | MPa | ISO 178 |
| Flexural Stress | 138 | 72.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 4.7 | 26 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 180 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | -- | °C | ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | DIN 53482 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.59 mm | HB | -- | ||
| 3.18 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Rear Temperature | 265 to 280 | °C | |
| Middle Temperature | 255 to 270 | °C | |
| Front Temperature | 255 to 270 | °C | |
| Nozzle Temperature | 240 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 60.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 205 TFE 13 | RTP Company | Nylon 66 | RTP |
| SABIC® PP 57MNK10 | SABIC Americas, Inc. | PP Impact Copolymer | SABIC® PP |
| Petro Rabigh PP AZ764 | Rabigh Refining & Petrochemical Co. | PP Impact Copolymer | Petro Rabigh PP |
| Hostacom TRC 333N D72645 | LyondellBasell Industries | PP Copolymer | Hostacom |
| LEXAN™ HFD4412 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |