RTP 100 HS
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GNMgcx_RTP-100-HS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.908 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 2.5 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 80 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1310 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 34.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 150 | % | ASTM D638 |
| Flexural Modulus | 1240 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 48.3 | MPa | ASTM D790 |
| Compressive Strength | 46.9 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 800 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 107 | °C | |
| 1.8 MPa, Unannealed | 54.4 | °C | |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.13 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.20 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 2.0E-4 | ASTM D150 | |
| Arc Resistance (1.59 mm) | 136 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.59 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 232 to 263 | °C | |
| Middle Temperature | 238 to 268 | °C | |
| Front Temperature | 243 to 274 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 138 | MPa | |
| Back Pressure | 0.172 to 0.345 | MPa | |
| Clamp Tonnage | 5.5 to 8.3 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nucrel® 3990L | DuPont Packaging & Industrial Polymers | EAA | Nucrel® |
| APICAL 100AV | Kaneka Corporation | PI, TS | APICAL |
| G-PAEK™ 1100G | Gharda Chemicals Ltd. | PEK | G-PAEK™ |
| Plaslube® PA6 GF20 RM L BK | Techmer Engineered Solutions | Nylon 6 | Plaslube® |
| Stat-Tech™ PP-16CP/000-2HI BLACK | PolyOne Corporation | PP, Unspecified | Stat-Tech™ |