Lucobit 1210AC

Category:	PE Copolymer , Polyethylene Copolymer
Manufacturer:	Lucobit AG
Trademark:	Lucobit
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GN8RcQ_Lucobit1210AC.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Lucobit® 1210AC is a mixture of ethylene copolymers and special bitumen. The resulting formulation is a concentrate or "masterbatch". Lucobit® 1210AC consists of thermoplastic polyolefins. Addition of Lucobit to bitumen increases its viscosity and broadens the range of plasticity. Depending on the proportion of Lucobit 1210AC that was added the minimum value of the Fraass breaking point of 1210AC modified bitumen decreases and the ring and ball softening point increases. Penetration values decline accordingly. Ductility determined according to DIN EN 12591 decreases, however, the values ascertained for the so-called ductility at low temperatures are more favourable than those for standard bitumen without addition of Lucobit. Compared with other standard binder Lucobit 1210AC displays significant advantages in improving resistance to deformation. Rut formation tests at high temperatures demonstrated that asphalt can bear a two- to threefold load when modifying it with thermoplastics or altering binder viscosity by adding Lucobit. The low temperature properties of Lucobit 1210AC modified asphalt also improve significantly. Applications Even relatively small amounts of Lucobit 1210A in asphalt mixtures improve: resistance to mechanical stress, in particular deformation and wear stability/rigidity and reduce the tendency to flow when hot and under load low temperature flexibility ageing behaviour Examples for application: s-wearing courses to ZTV-Asphalt - StB poured asphalt, also on sloping surfaces (ramps) stone mastic asphalt special asphalt surfaces, e.g. porous asphalt thin bituminous wearing courses (hot laying)

Message

Lucobit® 1210AC is a mixture of ethylene copolymers and special bitumen. The resulting formulation is a concentrate or "masterbatch".

Lucobit® 1210AC consists of thermoplastic polyolefins. Addition of Lucobit to bitumen increases its viscosity and broadens the range of plasticity. Depending on the proportion of Lucobit 1210AC that was added the minimum value of the Fraass breaking point of 1210AC modified bitumen decreases and the ring and ball softening point increases. Penetration values decline accordingly. Ductility determined according to DIN EN 12591 decreases, however, the values ascertained for the so-called ductility at low temperatures are more favourable than those for standard bitumen without addition of Lucobit.

Compared with other standard binder Lucobit 1210AC displays significant advantages in improving resistance to deformation. Rut formation tests at high temperatures demonstrated that asphalt can bear a two- to threefold load when modifying it with thermoplastics or altering binder viscosity by adding Lucobit. The low temperature properties of Lucobit 1210AC modified asphalt also improve significantly.

Applications
Even relatively small amounts of Lucobit 1210A in asphalt mixtures improve:

resistance to mechanical stress, in particular deformation and wear

stability/rigidity and reduce the tendency to flow when hot and under load

low temperature flexibility

ageing behaviour

Examples for application:

s-wearing courses to ZTV-Asphalt - StB

poured asphalt, also on sloping surfaces (ramps)

stone mastic asphalt

special asphalt surfaces, e.g. porous asphalt

thin bituminous wearing courses (hot laying)

General Information
Features	Chlorine Free Good dimensional stability Flexibility at low temperatures Rigidity, high Copolymer Environmental protection Good heat aging resistance Good stability
Uses	Asphalt modification Masterbatch
Appearance	Black
Forms	Particles

Physical	Nominal Value	Unit	Test Method
Density	0.970	g/cm³	ISO 1183
Apparent Density	0.50	g/cm³	ISO 60

Mechanical	Nominal Value	Unit	Test Method
Tensile Strain (Break, 23°C)	800 - 900	%	ISO 527-2

Resin Grade	Manufacturer	Category	Trademark
Manner Flexible PVC X4590U	Manner Plastics, L.P.	PVC, Flexible	Manner Flexible PVC
PrimoPrene 45D-1000	KMI Group Inc.	TPV	PrimoPrene
THERMOLAST® K TC6PAN (Series: AD/PA)	KRAIBURG TPE	TPE	THERMOLAST® K
LNP™ LUBRICOMP™ RFL26 compound	SABIC Innovative Plastics	Nylon 66	LNP™ LUBRICOMP™
Lucent TPO TPO-20NBS	Lucent Polymers, Inc.	Polyolefin, Unspecified	Lucent TPO