ULTEM™ 9085 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GMeQBY_ULTEM9085resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (295°C/6.6 kg) | 8.9 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (360°C/5.0 kg) | 65.5 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.39 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.17 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3440 | MPa | ASTM D638 |
| -- | 3050 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 84.0 | MPa | ASTM D638 |
| Yield | 88.0 | MPa | ISO 527-2/5 |
| Fracture 3 | 74.0 | MPa | ASTM D638 |
| Fracture | 71.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 7.0 | % | ASTM D638 |
| Yield | 6.7 | % | ISO 527-2/5 |
| Fracture 5 | 72 | % | ASTM D638 |
| Fracture | 50 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2920 | MPa | ASTM D790 |
| -- 7 | 2750 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 90.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 138 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 9 | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 153 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 10 | 152 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 173 | °C | ISO 306/B120 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 49 | % | ASTM D2863 |
| FAA Flammability 11 | FAR 25.853 | ||
| OSU peak heat release rate 12 | 36.0 | kW/m² | FAR 25.853 |
| OSU total heat release 13 | 16.0 | kW·min/m² | FAR 25.853 |
| Vertical Burn Test - Test a (60 s), passes at | 2.0 | sec | FAR 25.853 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 135 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 315 - 340 | °C | |
| Middle Temperature | 325 - 345 | °C | |
| Front Temperature | 330 - 350 | °C | |
| Nozzle Temperature | 330 - 350 | °C | |
| Processing (Melt) Temp | 330 - 350 | °C | |
| Mold Temperature | 120 - 150 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 100 | °C | |
| Cylinder Zone 1 Temp. | 265 - 275 | °C | |
| Cylinder Zone 2 Temp. | 280 - 295 | °C | |
| Cylinder Zone 3 Temp. | 290 - 305 | °C | |
| Cylinder Zone 4 Temp. | 295 - 310 | °C | |
| Adapter Temperature | 270 - 310 | °C | |
| Melt Temperature | 280 - 310 | °C | |
| Die Temperature | 260 - 310 | °C | |
| Calibration Temp, First | 130 - 160 | °C | |
| Calibration Temp, Second | 80.0 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | Type 1, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | Method A/B |
| 12 . | 5 minute test |
| 13 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVASTER® B GF 30 FRL 4 | Plastcom | PBT | SLOVASTER® |
| T-Blend® 6594N-WGS97 | TSRC Corporation | SEBS | T-Blend® |
| Vandar® 2122 | Celanese Corporation | PBT | Vandar® |
| Caltex PP HLG73 | GS Caltex | PP, Unspecified | Caltex PP |
| PENTAMID A GV25 MC25 H natural | PENTAC Polymer GmbH | Nylon 66 | PENTAMID A |