Generic EEA
| Category: | EEA , Ethylene Ethyl Acrylate Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GMeEK9_Generic-EEA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic EEA This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.930 to 0.940 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 190°C/2.16 kg | 1.0 to 21 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 0.40 to 6.1 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| 23°C | 26 to 87 | ASTM D2240 | |
| 23°C | 27 to 87 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break, 23°C | 5.50 to 17.9 | MPa | ASTM D638 |
| Break, 23°C | 5.96 to 10.1 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break, 23°C | 590 to 800 | % | ASTM D638 |
| Break, 23°C | 600 to 860 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 28.3 to 31.0 | MPa | ASTM D790 |
| 23°C | 22.8 to 77.8 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | |||
| -- | 40.0 to 65.5 | °C | ASTM D1525 |
| -- | 40.0 to 70.5 | °C | ISO 306 |
| Melting Temperature | |||
| -- | 65.0 to 112 | °C | DSC |
| -- | 94.7 to 104 | °C | ISO 3146 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICTREX® PEEK 150GL15 | Victrex plc | PEEK | VICTREX® PEEK |
| COSMOTHENE® EVA KA-40 | TPC, The Polyolefin Company (Singapore) Pte Ltd | LDPE | COSMOTHENE® EVA |
| Fainplast PVC RKS 320 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| Luran® S 778TE | Styrolution | ASA | Luran® S |
| LNP™ THERMOTUF™ VX00585 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |