Stat-Tech™ PC-08CF/000 NH FR BLACK
| Category: | PC , Polycarbonate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Stat-Tech™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GLtUIl_Stat-Tech-PC-08CF-000-NH-FR-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Carbon Fiber Filled, Non-Halogen Containing Flame Retardant Polycarbonate Compound |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage (3.00 mm) | 0.40 - 0.60 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 4800 | MPa | ASTM D638 |
| Tensile Strength 2 | 90.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus 4 | 5500 | MPa | ASTM D790 |
| Flexural Strength 5 | 145 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm, Injection Molded) | 90 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 139 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+2 - 5.0E+4 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 80.0 - 120 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Selvol™ 840 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| NOVA PC 1020 | NOVA Polymers, Inc. | PC | NOVA PC |
| Hifax TYC 1123P RXF Black | LyondellBasell Industries | TPO (POE) | Hifax |
| LNP™ THERMOCOMP™ PF004S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |
| TAFMER™ PN-2070 | Mitsui Chemicals, Inc. | PAO | TAFMER™ |