Hifax TRS 123D NAT
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GLqGzy_HifaxTRS123DNAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax TRS 123D NAT high melt flow, 950 MPa flexural modulus, natural, reactor grade thermoplastic elastomeric olefin (TEO) resin has an excellent balance of impact, stiffness, paintability, and processability. It is based on material produced from LyondellBasell's proprietary Catalloy process. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Density 1(23°C) | 0.890 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 17 | g/10 min |
| Mechanical | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 18.0 | MPa | |
| Tensile Elongation (Yield, 23°C) | 8.0 | % | |
| Flexural Modulus (23°C) | 950 | MPa |
| Impact | Nominal Value | Unit | |
|---|---|---|---|
| Notched Izod Impact (23°C) | 46 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy 2(-30°C, 3.20 mm) | 25.0 | J |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 80.0 | °C | |
| 1.8 MPa, not annealed | 53.0 | °C |
| Note Message | |
|---|---|
| 1 . | Method A |
| 2 . | 2.2 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SilTRUST® TSE3664K | Momentive Performance Materials Inc. | Silicone | SilTRUST® |
| Telcar® TL-1025-85 | Teknor Apex Company | TPE | Telcar® |
| ABSplus™ P430 | Stratasys | ABS | ABSplus™ |
| Geon™ HTX Ultra LA426 Tan 3725 | PolyOne Corporation | PVC Alloy | Geon™ HTX Ultra |
| TOTAL Polypropylene Aceso® PPM R020 S01 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |