Wellamid® 42LH-N
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Wellman Engineering Resins |
| Trademark: | Wellamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GLHfmy_Wellamid-42LH-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Wellamid® 42LH-N is a Polyamide 6 (Nylon 6) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Wellamid® 42LH-N: Flame Rated. Typical application of Wellamid® 42LH-N: Automotive |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 23°C | 1.2 to 1.6 | % | |
| Flow : 23°C | 1.1 to 1.5 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 75.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 40 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 95.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 5.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 55.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 238 to 282 | °C | |
| Middle Temperature | 232 to 277 | °C | |
| Front Temperature | 227 to 271 | °C | |
| Nozzle Temperature | 227 to 293 | °C | |
| Processing (Melt) Temp | 227 to 293 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C | |
| Injection Pressure | 34.5 to 138 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Screw Speed | 30 to 120 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® EHM 6007 | Chevron Phillips Chemical Company LLC | HDPE | Marlex® |
| Tislamid® PA66 PA66 25 GBR | Tisan | Nylon 66 | Tislamid® PA66 |
| KetaSpire® KT-820 CF30 | Solvay Specialty Polymers | PEEK | KetaSpire® |
| ISOTHANE® 2080A | Great Eastern Resins Industrial Co Ltd (GRECO) | TPU-Polyester | ISOTHANE® |
| Karina WHITE MINERAL CONC. MBU -E 10/0085-IE | Karina Ind. e Com. de Plásticos Ltda | EVA | Karina |