Alathon® M5372
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Alathon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GK8ziS_Alathon-M5372.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ALATHON M5372 is a copolymer with narrow molecular weight distribution. This resin provides high impact strength and stress crack resistance, excellent color, low odor and good processing stability. Typical applications include open head pails and large shipping containers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ASTM D1505 |
| Apparent Density | 0.59 to 0.63 | g/cm³ | ASTM D1895 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.9 | g/10 min | ASTM D1238 |
| Spiral Flow | 22.4 | cm | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | ASTM D638 | ||
| -- | 911 | MPa | |
| 1% Secant | 765 | MPa | |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 27.2 | MPa | |
| Break | 21.9 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 11 | % | |
| Break | 1200 | % | |
| Flexural Modulus 4 | ASTM D790 | ||
| -- | 1290 | MPa | |
| 1% Secant | 1190 | MPa | |
| 2% Secant | 977 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 48 | J/m | ASTM D256 |
| Unnotched Izod Impact (-18°C) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 70.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 127 | °C | ASTM D1525 |
| Peak Melting Temperature | 131 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 116 | °C | ASTM D3418 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 232 | °C | |
| Middle Temperature | 243 | °C | |
| Front Temperature | 246 | °C | |
| Nozzle Temperature | 246 | °C |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| 4 . | 13 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vikalloy P45 | Viking Polymers, LLC | CPVC | Vikalloy |
| TRANSMARE® 14CGF20-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| Aaroprene® ATPR 2000 80A | Aaron Industries Corp. | TPE | Aaroprene® |
| Boda BDP-H9701 | Chenguang Fluoro & Silicone Elastomers Co., Ltd. | Fluorelastomer | Boda |
| CALP FR913-1 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |