SABIC® PPcompound 8611P resin
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GK6BPP_SABIC-PPcompound-8611P-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 8611P is a mineral filled, impact modified polypropylene TPO. This material combines scratch resistance and good flow with exterior automotive weathering stability. It was originally designed for painted or unpainted automotive bumper fascia applications where a combination of low density, high stiffness and cold temperature ductility is required. The IMDS is 482236763 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.968 | g/cm³ | ASTM D792 |
| -- | 0.960 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 34 | g/10 min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 80°C, 1 hr | 1.1 | % | |
| Across Flow : 120°C, 30 min | 1.1 | % | |
| Across Flow : 23°C, 48 hr | 0.95 | % | |
| Flow : 80°C, 1 hr | 0.60 | % | |
| Flow : 120°C, 30 min | 0.71 | % | |
| Flow : 23°C, 48 hr | 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1650 | MPa | ISO 527-2/1 |
| Tensile Stress | |||
| Yield | 19.0 | MPa | ISO 527-2/50 |
| Break | 13.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Break) | 100 | % | ISO 527-2/50 |
| Flexural Modulus 1(64.0 mm Span) | 1760 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 2 | 6.0 | kJ/m² | |
| 23°C 3 | 34 | kJ/m² | |
| Notched Izod Impact Strength 4 | ISO 180/1A | ||
| 0°C | 30 | kJ/m² | |
| 23°C | 41 | kJ/m² | |
| Instrumented Dart Impact 5 | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 24.0 | J | |
| 23°C, Energy at Peak Load | 22.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, Unannealed | 100 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 53.0 | °C | ISO 75-2/A |
| Coefficient of Linear Thermal Expansion | ISO 11359-2 | ||
| Flow : -30 to 100°C | 49.0 | µm/Mk | |
| Transverse : -30 to 100°C | 127 | µm/Mk |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Rear Temperature | 190 to 230 | °C | |
| Middle Temperature | 200 to 250 | °C | |
| Front Temperature | 210 to 270 | °C | |
| Nozzle Temperature | 210 to 270 | °C | |
| Processing (Melt) Temp | 210 to 270 | °C | |
| Mold Temperature | 15.0 to 60.0 | °C | |
| Back Pressure | 1.00 to 1.50 | MPa |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4mm, Cut |
| 3 . | 80*10*4 mm, Cut |
| 4 . | 80*10*4mm, Cut |
| 5 . | 2.20 m/sec |
| 6 . | 80*10*4mm, Cut |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209E | RTP Company | Nylon, Unspecified | RTP |
| RTP 801 DEL UV | RTP Company | Acetal (POM) Homopolymer | RTP |
| Calprene® 401 | Dynasol Elastomers | SBS | Calprene® |
| Epoxies, Ect. 10-3062 | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| LNP™ THERMOCOMP™ LX09409 compound | SABIC Innovative Plastics | PEEK | LNP™ THERMOCOMP™ |