FORMULA P COMP 5410 M1
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GIBOb7_FORMULA-P-COMP-5410-M1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FORMULA P COMP 5410 M1 is a polypropylene product,. It is available in Europe. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.950 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 15 | g/10 min | ISO 1133 |
| Molding Shrinkage | 1.0 - 1.2 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 26.0 | MPa | ISO 527-2 |
| Fracture | 23.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 50 | % | ISO 527-2 |
| Flexural Modulus | 2000 | MPa | ISO 178 |
| Scratch Resistance 1 | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 10 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 72.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 26 MPa |
| Note Message | |
|---|---|
| 1 . | At 10 NTest method: Erichsen Test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® G black B 100 | Röchling Engineering Plastics SE & Co. KG | HDPE | POLYSTONE® |
| megol® DP1741 85 | API SpA | SEBS | megol® |
| Wondel® T PETR0G6 | Nanjing Julong Engineering Plastics Co., LTD | PET | Wondel® T |
| Chemlon® MDT10 | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| RONFALIN® ABS 1220 MW 20 U | A. Schulman Europe | ABS | RONFALIN® |