Orgalloy® RS 6620
| Category: | Nylon 66 Alloy , Polyamide 66 Alloy |
| Manufacturer: | Arkema |
| Trademark: | Orgalloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GHwPvx_Orgalloy-RS-6620.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Orgalloy® RS 6620 is a Polyamide 66 Alloy (Nylon 66 Alloy) product filled with filler. It can be processed by extrusion, injection molding, profile extrusion, or resin transfer molding and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Primary characteristic: heat resistant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1180 | 1180 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate (275°C/2.16 kg) | 10.0 | -- | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | |||
| Saturation | 2.3 | -- | % | |
| Equilibrium | 1.1 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | -- | 5500 | MPa | ISO 527-2 4 |
| Tensile Stress (Break) | -- | 110 | MPa | ISO 527-2 5 |
| Tensile Strain (Break) | -- | 4.5 | % | ISO 527-2 6 |
| Tensile Creep Modulus | ISO 899-1 7 | |||
| 1 hr | -- | 4900 | MPa | |
| 1000 hr | -- | 3510 | MPa |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 8 | |||
| 0.45 MPa | 240 | -- | °C | |
| 1.8 MPa | 220 | -- | °C | |
| Vicat Softening Temperature (50°C/h, B (50N)) | 160 | -- | °C | ISO 306 9 |
| Melting Temperature 10 | 255 | -- | °C | ISO 11357-3 11 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface resistivity | -- | > 1.0E+15 | ohms | IEC 60093 12 |
| Volume resistivity | -- | > 1.0E+13 | ohms·m | IEC 60093 13 |
| Electric strength | 35 | 35 | kV/mm | IEC 60243-1 14 |
| Relative Permittivity | IEC 60250 15 | |||
| 100 Hz | -- | 3.00 | ||
| 1 MHz | -- | 4.00 | ||
| Dissipation Factor | IEC 60250 16 | |||
| 100 Hz | -- | 0.028 | ||
| 1 MHz | -- | 0.017 | ||
| Comparative tracking index | -- | 600 | IEC 60112 17 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | -- | ISO 1210 18 | |
| Burning Behav. at thickness h (3.20 mm) | HB | -- | ISO 1210 19 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | 10 °C/min |
| 11 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 17 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 18 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 19 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| METALCAP PPC382C87 | Polyram Ram-On Industries | PP Copolymer | METALCAP |
| Starex WX-9700 | SAMSUNG SDI CO., LTD. | ASA | Starex |
| Bergamid™ A70 G50 H Natural | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Evermore PUR UP-9330N | Evermore Chemical Industry Co., Ltd. | PUR-Ether | Evermore PUR |
| MAJ'ECO DP374HGM | AD majoris | PP, Unspecified | MAJ'ECO |