Zytel® BM7300THS BK317
| Category: | Nylon 6 , NYLON RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GHwMR2_ZytelBM7300THSBK317.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Toughened, Heat Stabilized, Polyamide 6 Developed for Blow Molding |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.09 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Transverse flow | 1.1 | -- | % | ISO 294-4 |
| Flow | 1.1 | -- | % | ISO 294-4 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2200 | 600 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 60.0 | -- | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.2 | -- | % | ISO 527-2 |
| Nominal Tensile Strain at Break | > 50 | -- | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 21 | 22 | kJ/m² | ISO 179/1eA |
| 23°C | 45 | 150 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C 1 | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/1A | |||
| -30°C | 18 | 20 | kJ/m² | ISO 180/1A |
| 23°C | 38 | 120 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 100 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 52.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 2 | 220 | -- | °C | ISO 11357-3 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 3(1.00 mm) | < 100 | -- | mm/min | ISO 3795 |
| FMVSS Flammability | B | -- | FMVSS 302 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Melt Temperature, Optimum | 270 | °C | |
| Mold Temperature, Optimum | 70 | °C | |
| Drying Recommended | yes | ||
| Hold Pressure Time | 3.00 | s/mm | |
| Maximum Screw Tangential Speed | 200 | mm/sec |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Viscosity (280°C, 1000 sec^-1) | 440000 | -- | mPa·s | ISO 11443 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time - Desiccant Dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 50 - 100 | °C | |
| Holding Pressure | 50.0 - 100 | MPa |
| Note Message | |
|---|---|
| 1 . | Assessed |
| 2 . | 10°C/min |
| 3 . | FMVSS 302 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICTREX® PEEK 450PF | Victrex plc | PEEK | VICTREX® PEEK |
| Epic Urethane S7475 | Epic Resins | PUR, Unspecified | Epic Urethane |
| Lupoy® 1303-07 | LG Chem Ltd. | PC | Lupoy® |
| Sylvin 2987-80 Clear 8422 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9077-70 Yellow 4113 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |