Ravamid® AMGF15/15 H BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ravago Group |
| Trademark: | Ravamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGovSn_Ravamid-AMGF15-15-H-BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Black, 15% mineral filled, 15% glass fibre reinforced, heat stabilized All the products are also available Heat Stabilized (H) and UV Stabilized (UV) |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Recycled Content |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.55 to 0.90 | % | ASTM D955 |
| Humidity | < 0.20 | % | ISO 960 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ASTM D882, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 85.0 | MPa | |
| Break | 80.0 | MPa | |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 5600 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 215 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 240 | °C | ISO 306/B50, ASTM D1525 1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (3.20 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Note Message | |
|---|---|
| 1 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9950C | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Precision Polymer V61C | Precision Polymer Engineering Ltd. | Fluorelastomer | Precision Polymer |
| Niuk 10TP20 | Shanghai Niuk New Plastic Technology Co., Ltd. | PP, Unspecified | Niuk |
| Borealis PP ZC135 | Borealis AG | TPO | Borealis PP |
| ECONAMID庐 66FLST1 | DOMO Engineering Plastics SPA | Nylon 66 | ECONAMID® |