Arylmax® K7522CF30
| Category: | PAEK , Polyaryletherketone |
| Manufacturer: | Polymics, Ltd. |
| Trademark: | Arylmax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGc4FO_Arylmax-K7522CF30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyaryletherketone, Easy Flow, 30% carbon filled |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.040 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 100 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 28000 | MPa | ASTM D638 |
| Tensile Strength | 248 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.2 | % | ASTM D638 |
| Flexural Modulus | 24000 | MPa | ASTM D790 |
| Flexural Strength | 368 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 5.0 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 321 | °C | ASTM D648 |
| Glass Transition Temperature | 171 | °C | ASTM D3418 |
| Melting Temperature | 352 | °C | DSC |
| CLTE - Flow | 3.6E-5 | cm/cm/°C | ASTM D696 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM C177 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 50 | ohms | ASTM D257 |
| Volume Resistivity | 50 | ohms·cm | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PONACOM PS 5360 | Ponachem Compound GmbH | PS (HIPS) | PONACOM PS |
| RTP 282 TFE 10 | RTP Company | Nylon 66 | RTP |
| Reny® NXG5050NF | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| Delta PPR-1CG80 | Delta Polymers | PP Homopolymer | Delta |
| Ingeo™ AW 300D | NatureWorks® LLC | PLA | Ingeo™ |