Geon™ HTX Ultra LA425
| Category: | PVC Alloy , Polyvinyl Chloride Alloy |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ HTX Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGY3Oo_Geon-HTX-Ultra-LA425.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| It is most suitable for black and darker colors with color values lower than 50L. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 4-42411-64-0000 | ASTM D4216 | |
| PVC Cell Classification | 15225 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 74 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 1990 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 37.9 | MPa | ASTM D638 |
| Flexural Modulus | 2080 | MPa | ASTM D790 |
| Flexural Strength | 66.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm, Compression Molded) | 720 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C 3 | 66.7 | J/cm | ASTM D4226 |
| 23°C 4 | 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 90.6 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 91.1 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 83.9 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 87.2 | °C | ASTM D648 |
| CLTE - Flow | 8.6E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Acceptable | ||
| 推荐在华氏160度下将材料干燥至少2小时。通过仪器化冲击测量的韧性/脆化转变5 deg.C 物理属性基于 Geon HTX Ultra LA425 Natural 0000 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 174 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Procedure A, C.125 Throwing |
| 4 . | Procedure B, C.125 Throwing |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® Polyester TC 197 | Saudi Basic Industries Corporation (SABIC) | PET | SABIC® HDPE |
| Elastollan® WY1157 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Karina IVORY PVC COMPOUND 105900-35/1-B-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Karina IVORY PVC COMPOUND -E 807D35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ LUBRICOMP™ IFL34 compound | SABIC Innovative Plastics | Nylon 612 | LNP™ LUBRICOMP™ |