LUBEMIX 65 BLACK
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LUBEN PLAST srl |
| Trademark: | LUBEMIX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GGINSF_LUBEMIX-65-BLACK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Compound based on blend PC/ABS second choice. Black coloured. |
| General Information | |
|---|---|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 to 1.15 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (260°C/5.0 kg) | 15 to 20 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1800 to 2000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress | ISO 527-2/1A/50 | ||
| Yield | 40.0 to 45.0 | MPa | |
| Break | 40.0 to 45.0 | MPa | |
| Tensile Strain | ISO 527-2/1A/50 | ||
| Yield | 4.0 to 6.0 | % | |
| Break | 35 to 40 | % | |
| Flexural Modulus 1 | 1800 to 2200 | MPa | ISO 178 |
| Flexural Stress 2 | 45.0 to 50.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 35 to 40 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| 23°C, 3.20 mm | 400 to 450 | J/m | ASTM D256A |
| 23°C 3 | No Break | ASTM D256 | |
| 23°C | 35 to 40 | kJ/m² | ISO 180/A |
| 23°C 4 | 40 to 45 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength (23°C) | No Break | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 115 to 125 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 120 to 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed, 3.20 mm | 100 to 110 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 125 to 135 | °C | ISO 306/A120 |
| -- | 120 to 130 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Notch E |
| 4 . | Notch A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7120B | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Quadrant EPP Delrin® Acetal | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| Karina IVORY PVC COMPOUND -E 60820-35/1-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ VERTON™ RV00CES compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| SIBUR Synthetic Rubber NBR 2665 | SIBUR | NBR | SIBUR Synthetic Rubber |