Ultramid® B3GK24
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GG7LUX_Ultramid-B3GK24.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3GK24 is 30% combined glass-fiber and glass bead injection molding PA6 grade for industrial articles having very high dimensional stability. Applications Typical applications include automobile ashtrays and housings for electronics. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.34 | -- | g/cm³ | ASTM D792, ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 70.0 | -- | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 | -- | % | |
| Water Absorption | ||||
| Saturation | 6.6 | -- | % | ASTM D570 |
| Saturation, 23°C | 6.6 | -- | % | ISO 62 |
| Equilibrium, 50% RH | 2.0 | -- | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 6000 | 3000 | MPa | ISO 527-2 |
| Tensile Strength | ||||
| Break, 23°C | 110 | -- | MPa | ASTM D638 |
| Break, 23°C | 105 | 60.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.5 | 15 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 4830 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 5.0 | 11 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 39 | -- | kJ/m² | |
| 23°C | 40 | 90 | kJ/m² | |
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 32 | -- | J/m | |
| 23°C | 37 | -- | J/m |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 200 | -- | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 220 | -- | °C | ASTM D3418, ISO 3146 |
| CLTE - Flow | ||||
| -- | 1.0E-5 | -- | cm/cm/°C | ASTM E831 |
| -- | 3.8E-5 | -- | cm/cm/°C | |
| RTI Elec | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Imp | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C | |
| RTI Str | UL 746 | |||
| 0.750 mm | 65.0 | -- | °C | |
| 1.50 mm | 65.0 | -- | °C | |
| 3.00 mm | 65.0 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | ||||
| 1.50 mm | 1.0E+15 | 1.0E+12 | ohms·cm | ASTM D257 |
| -- | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.90 | 4.60 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.020 | 0.070 | IEC 60250 | |
| Comparative Tracking Index | 425 | 425 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.12 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide AN-18 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| Clyrell RC249R | LyondellBasell Industries | PP Random Copolymer | Clyrell |
| Hanwha Total PP HI831 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| ICORENE® N2103 | ICO Polymers EMEA, A Division of A. Schulman | LDPE | ICORENE® |
| apigo bio® PM 1000 | API SpA | TPO (POE) | apigo bio® |