MALAT 38GFRH200 - 1298
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | AD majoris |
| Trademark: | MALAT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GFyxOE_MALAT-38GFRH200---1298.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MALAT 38GFRH200 - 1298 is a Polybutylene Terephthalate (PBT) product filled with glass fiber. It can be processed by injection molding and is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | NF T 51-063 |
| Molding Shrinkage 1 | |||
| Across Flow : 3.00 mm | 0.80 | % | |
| Flow : 3.00 mm | 0.60 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 0.030 | % | NF T 51-166 |
| Equilibrium, 23°C, 50% RH | 0.14 | % | NF T 51-290 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8200 | MPa | NF T 51-034 |
| Tensile Stress (Break) | 115 | MPa | NF T 51-034 |
| Tensile Strain (Break) | 2.5 | % | NF T 51-034 |
| Flexural Modulus | 7600 | MPa | NF T 51-001 |
| Flexural Stress 2 | 180 | MPa | NF T 51-001 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.5 | kJ/m² | NF T 51-035 |
| Charpy Unnotched Impact Strength | 30 | kJ/m² | NF T 51-035 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | NF T 51-005 | ||
| 0.45 MPa, Unannealed | 215 | °C | |
| 1.8 MPa, Unannealed | 205 | °C | |
| Ball Pressure Test (215°C) | Pass | NF C 62-411 | |
| Melting Temperature (DSC) | 225 | °C | NF T 51-049 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | NF C 26-215 |
| Volume Resistivity | 1.0E+15 | ohms·cm | NF C 26-215 |
| Electric Strength (2.00 mm) | 21 | kV/mm | NF C 26-225 |
| Comparative Tracking Index | NF C 26-220 | ||
| Solution A | 250 | V | |
| Solution B | 125 | V | |
| Insulation Resistance | 1.0E+14 | ohms | NF C 26-210 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | NF T 51-072 | |
| Glow Wire Flammability Index (1.60 mm) | 960 | °C | DIN 57471 |
| Oxygen Index | 31 | % | NF T 51-071 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 230 to 240 | °C | |
| Middle Temperature | 240 to 250 | °C | |
| Front Temperature | 250 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Plate 100x100x3 mm |
| 2 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Solprene® 303 | Dynasol Elastomers | SBR, Solution | Solprene® |
| Sylvin 29168-70 Clear 8382 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sup-tech A709 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 66 | Sup-tech |
| HiFill® POM CO GF25 CC | Techmer Engineered Solutions | Acetal (POM) Copolymer | HiFill® |
| Karina STRAW CPVC COMPOUND 790-38/23-CRPC (**) | Karina Ind. e Com. de Plásticos Ltda | CPVC | Karina |