Order Products : sales@su-jiao.com
Hanwha Total PP BJ51W
| Category: | PP, High Crystal , High Crystallinity Polypropylene |
| Manufacturer: | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Trademark: | Hanwha Total PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GFhv76_Hanwha-Total-PP-BJ51W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BJ51W is a polypropylene compound with super weatherability and is ideal for use in outdoor products such as the exteriors of air-conditioning systems. This grade uses a base PP, such as HIPP (High Isotactic Polypropylene), and is manufactured with special processing technology to provide customers with a product of the best quality. This grade possess heightened rigidity, impact-resistance, long-term heat-resistance, as well as protection against thermal discoloration and anti-static property. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (2.00 mm) | 1.4 to 1.8 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 27.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 500 | % | ASTM D638 |
| Apparent Bending Modulus | 34.3 | MPa | ASTM D747 |
| Flexural Modulus 3 | 1270 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 105 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 180 to 200 | °C | |
| Middle Temperature | 190 to 210 | °C | |
| Front Temperature | 200 to 220 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C | |
| Injection Pressure | 58.8 to 98.1 | MPa | |
| Holding Pressure | 39.2 to 88.3 | MPa | |
| Screw Speed | 30 to 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE HP2023J | SABIC Americas, Inc. | LDPE | SABIC® LDPE |
| Europrene Latice® 5570 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |
| Durethan® BKV 35 H2.0 EF 901510 | LANXESS GmbH | Nylon 6 | Durethan® |
| Gallonprene® GP520-6016 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| SQUARE® LSG6931-20A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |