EPO-TEK® 302
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GFQI5k_EPO-TEK-302.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPO-TEK® 302 is a two component, fast-gelling, room temperature curing epoxy, designed for electronic, optical, medical, and general applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 40.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 5.2E-5 | cm/cm/°C | |
| -- 3 | 1.9E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.544 | ||
| Transmittance | |||
| 340 to 420 nm | > 75.0 | % | |
| 440 to 900 nm | > 85.0 | % | |
| 900 to 1600 nm | > 88.0 | % |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 1.0 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 43 | wk |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Degradation Temperature | 261 | °C | TGA |
| Die Shear Strength - >5 kg (23°C) | 11.7 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 100 | °C | |
| Intermittent | -55 to 200 | °C | |
| Storage Modulus (23°C) | 1.06 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 2.7 | % | |
| 250°C | 8.4 | % |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 5 | Clear/Transparent | ||
| -- 6 | Clear/Transparent | ||
| Density | |||
| Part B | 0.898 | g/cm³ | |
| Part A | 1.20 | g/cm³ | |
| Viscosity 7(23°C) | 5.0 to 10 | Pa·s | |
| Curing Time (23°C) | 2.0 | hr | |
| Pot Life | 10 | min |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 73 | ||
| Lap Shear Strength (23°C) | 12.1 | MPa | |
| Relative Permittivity (1 kHz) | 2.95 | ||
| Volume Resistivity (23°C) | > 2.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.010 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part B |
| 6 . | Part A |
| 7 . | 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218G2 V30 BLACK 34 N | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| ELIX™ ABS M3FR | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| GETILAN GPE/409 AFM | Crosspolimeri S.p.A. | XLPE | GETILAN |
| Pier One PC/ABS C1200 BK | Pier One Polymers, Inc. | PC+ABS | Pier One PC/ABS |
| LNP™ STAT-KON™ RE002 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |