Akulon® K125/A
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | DSM Engineering Plastics |
| Trademark: | Akulon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GF88Sr_Akulon-K125-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Akulon® K125/A is a Polyamide 6 (Nylon 6) material. It is available in Europe. Primary attribute of Akulon® K125/A: Low Viscosity. |
| General Information | |
|---|---|
| Features |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | |
| Viscosity Number | 152 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3200 | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 85.0 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.0 | 25 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 20 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2600 | -- | MPa | ISO 178 |
| Flexural Stress | 100 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 8.0 | 35 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 230 to 235 | °C | |
| Middle Temperature | 235 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 270 | °C | |
| Processing (Melt) Temp | 240 to 275 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 3.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Razalen® Q111 | Razin™ Engineering Plastics | PP Homopolymer | Razalen® |
| Medalist® MD-12362 | Teknor Apex Company | TPE | Medalist® |
| Tarflen® SM-B40 | Grupa Azoty S.A. | PTFE | Tarflen® |
| ColorFast® PCT1000 | LTL Color Compounders, Inc. | PC+PET | ColorFast® |
| Gallonprene® GP310-7502 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |