Andur 8-5 APLF/Curene® 442
| Category: | PUR-Ester/TDI , Polyurethane (Polyester, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GElLIC_Andur-8-5-APLF-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 8-5 APLF is a polyester based liquid, toluene diisocyanate terminated prepolymer containing 0.1% or less free TDI monomer. An elastomer with a hardness of 84 to 86 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by reaction with various polyols and their combination with Curene 442, other diamines or through the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.25 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.34 | MPa | ASTM D412 |
| 300% strain | 8.79 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 46.2 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 650 | % | ASTM D412 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 5.5 - 6.0 | min | |
| Demold Time (100°C) | 30 | min | |
| Post Cure Time (100°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 84 to 86Die C Tear, ASTM D1004: 475 pliAverage Split Tear, ASTM D1938: 300 pliStoichiometry Curative Level: 95%Mix Temperature: Andur 8-5 APLF: 160-180°F Curene 442: 230-240°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP EI5003 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Stylac™ 190 | Asahi Kasei Chemicals Corporation | ABS | Stylac™ |
| Wellamid® FRGF1827-BK1 | Wellman Engineering Resins | Nylon 66 | Wellamid® |
| Ultramid® 1403-2 NF3001 | BASF Corporation | Nylon 66 | Ultramid® |
| EPO-TEK® T7109-17 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |