RTP 2503 A
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GEXIkF_RTP-2503-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Warning: The status of this material is 'Commercial: Limited Issue' The data for this material has not been recently verified. Please contact RTP Company for current information prior to specifying this grade. -Preliminary Product Data per RTP Co.- |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 0.20 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.12 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6890 | MPa | ASTM D638 |
| Tensile Strength | 103 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 30 | % | ASTM D638 |
| Flexural Modulus | 6210 | MPa | ASTM D790 |
| Flexural Strength | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.18 mm) | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 135 | °C | ASTM D648 |
| Additional Information |
|---|
| Mold Shrinkage, Linear-Flow, ASTM D955, 0.25in.: 3mil/in. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 98.9 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 232 - 288 | °C | |
| Middle Temperature | 232 - 288 | °C | |
| Front Temperature | 232 - 288 | °C | |
| Mold Temperature | 71.1 - 98.9 | °C | |
| Injection Pressure | 68.9 - 103 | MPa | |
| Back Pressure | 0.345 | MPa | |
| Clamp Tonnage | 6.9 - 11 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® MB 3000 NAT | Arkema | Nylon 11 | Rilsan® |
| Zythane® 6070D | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| LubriOne™ NL-30GF/15T Black | PolyOne Corporation | Nylon 612 | LubriOne™ |
| Pearlthane® MAXI 12T85E | Lubrizol Advanced Materials, Inc. | TPU-Polyester | Pearlthane® |
| Sumiliteresin® PR-54361 I | SBHPP | Phenolic | Sumiliteresin® |