Petro Rabigh PE F0554
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Rabigh Refining & Petrochemical Co. |
| Trademark: | Petro Rabigh PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GDslat_Petro-Rabigh-PE-F0554.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
F0554 is a high molecular weight high density polyethylene resin designed for blown film applications. This resin has broad molecular weight distribution that makes it easier to process. Films made from this resin exhibit high stiffness, excellent impact and toughness characteristics. Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.951 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.050 | g/10 min | |
| 190°C/21.6 kg | 9.3 | g/10 min |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 20 µm 1 | 990 | MPa | |
| 1% Secant, MD : 20 µm 2 | 930 | MPa | |
| 1% Secant, TD : 20 µm 3 | 1140 | MPa | |
| 1% Secant, TD : 20 µm 4 | 1030 | MPa | |
| Tensile Strength | |||
| MD : Yield, 20 µm 5 | 35.0 | MPa | ASTM D882 |
| TD : Yield, 20 µm 6 | 30.0 | MPa | ASTM D882 |
| MD : Break, 20 µm 7 | 75.0 | MPa | ASTM D882 |
| MD : Break, 20 µm 8 | 70.0 | MPa | ASTM D882 |
| TD : Break, 20 µm 9 | 55.0 | MPa | ASTM D882 |
| TD : Break, 20 µm 10 | 65.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm 11 | 520 | % | |
| MD : Break, 20 µm 12 | 560 | % | |
| TD : Break, 20 µm 13 | 560 | % | |
| TD : Break, 20 µm 14 | 550 | % | |
| Dart Drop Impact | ASTM D1709 | ||
| 20 µm 15 | 250 | g | |
| 20 µm 16 | 330 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm 17 | 11 | g | |
| MD : 20 µm 18 | 17 | g | |
| TD : 20 µm 19 | 78 | g | |
| TD : 20 µm 20 | 39 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature 21 | 126 | °C | ASTM D1525 22 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 180 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | With Stabilizer |
| 2 . | Without Stabilizer |
| 3 . | With Stabilizer |
| 4 . | Without Stabilizer |
| 5 . | With Stabilizer |
| 6 . | With Stabilizer |
| 7 . | With Stabilizer |
| 8 . | Without Stabilizer |
| 9 . | With Stabilizer |
| 10 . | Without Stabilizer |
| 11 . | With Stabilizer |
| 12 . | Without Stabilizer |
| 13 . | With Stabilizer |
| 14 . | Without Stabilizer |
| 15 . | With Stabilizer |
| 16 . | Without Stabilizer |
| 17 . | With Stabilizer |
| 18 . | Without Stabilizer |
| 19 . | With Stabilizer |
| 20 . | Without Stabilizer |
| 21 . | Without Stabilizer |
| 22 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer KE-2090-10A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| Staramide BG6ST43 | Eurostar Engineering Plastics | Nylon 6 | Staramide |
| Wondel® A AN0F | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| TYNEC® V1200 | Tyne Plastics LLC. | PC | TYNEC® |
| Alpha PVC AG K580D-N14A NATURAL | AlphaGary | PVC Elastomer | Alpha PVC |