ULTEM™ 9075 resin
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GDp7uB_ULTEM9075resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (340°C/5.0 kg) | 15.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.60 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 1.3 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.70 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 127 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 90.0 | MPa | ISO 527-2/50 |
| Fracture | 75.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture | 25 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 3200 | MPa | ISO 178 |
| Flexural Stress 3 | ISO 178 | ||
| -- 4 | 130 | MPa | ISO 178 |
| -- 5 | 120 | MPa | ISO 178 |
| Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 15.0 | mg | Internal method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6 | ISO 179/1eA | ||
| -30°C | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact 7 | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, unannealed, 100 mm span | 200 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 100 mm span | 185 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 210 | °C | ISO 306/A50 |
| -- | 200 | °C | ISO 306/B50, ISO 306/B120 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 | |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Horizontal : 23 to 150°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | 0.26 | W/m/K | ISO 8302 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm, Testing by SABIC) | V-0 | UL 94 | |
| Glow Wire Flammability Index (3.20 mm) | 960 | °C | IEC 60695-2-12 |
| OSU peak heat release rate 9 | 16.0 | kW/m² | FAR 25.853 |
| OSU total heat release 10 | 0.00 | kW·min/m² | FAR 25.853 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 160 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 120 | °C | |
| Rear Temperature | 320 - 340 | °C | |
| Middle Temperature | 345 - 365 | °C | |
| Front Temperature | 360 - 380 | °C | |
| Nozzle Temperature | 360 - 380 | °C | |
| Processing (Melt) Temp | 360 - 380 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 - 140 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 80.0 - 100 | °C | |
| Cylinder Zone 1 Temp. | 280 - 300 | °C | |
| Cylinder Zone 2 Temp. | 295 - 320 | °C | |
| Cylinder Zone 3 Temp. | 305 - 330 | °C | |
| Cylinder Zone 4 Temp. | 310 - 335 | °C | |
| Adapter Temperature | 285 - 335 | °C | |
| Melt Temperature | 295 - 330 | °C | |
| Die Temperature | 275 - 330 | °C | |
| Calibration Temp, First | 140 - 170 | °C | |
| Calibration Temp, Second | 90.0 - 130 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | Yield |
| 5 . | Break |
| 6 . | 80*10*4 sp=62mm |
| 7 . | 80*10*4 |
| 8 . | 120*10*4 mm |
| 9 . | 5 minute test |
| 10 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren F500EP (1st-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Random Copolymer | Sanren |
| NAXALOY® 793A3 GF10 | MRC Polymers, Inc. | PC+Polyester | NAXALOY® |
| Chemlon® 133 GU | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| FERREX® GPP20CF57HB-GY | Ferro Corporation | PP, Unspecified | FERREX® |
| Grilon® CF 7 | EMS-GRIVORY | Nylon 6/12 | Grilon® |