Laramid G/50
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laramid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GCzddW_Laramid-G-50.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Semi-aromatic polyammide. Glass fibres. Very good thermal properties. Good chemical resistance. Low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.64 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.65 to 0.95 | % | |
| Flow : 2.00 mm | 0.20 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 19000 | MPa | |
| 60°C | 14000 | MPa | |
| 90°C | 10500 | MPa | |
| 120°C | 8500 | MPa | |
| 150°C | 7200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 260 | MPa | |
| Break, 60°C | 205 | MPa | |
| Break, 90°C | 185 | MPa | |
| Break, 120°C | 165 | MPa | |
| Break, 150°C | 100 | MPa | |
| Tensile Strain | |||
| Break, 23°C | 2.4 | % | ISO 527-2/5 |
| Break, 60°C | 2.9 | % | ISO 527-2/5 |
| Break, 90°C | 3.7 | % | ISO 527-2/5 |
| Break, 120°C | 6.0 | % | ISO 527-2/1/5 |
| Break, 150°C | 7.0 | % | ISO 527-2/5 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 75 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 290 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 280 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 140 | °C | |
| Vicat Softening Temperature | 275 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 4.0E-6 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 310 to 340 | °C | |
| Mold Temperature | 150 to 170 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Precision Polymer N93H | Precision Polymer Engineering Ltd. | NBR | Precision Polymer |
| Tarflen® ST | Grupa Azoty S.A. | PTFE | Tarflen® |
| Tritan™ TX1001 | Eastman Chemical Company | Copolyester | Tritan™ |
| HAIPLEN H50 C12 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |
| Karina CRYSTAL PVC COMP. -E 75/328-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |