TARONYL G4
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TARONYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GClivs_TARONYL-G4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPO 20% glass fibres reinforced, low shrinkage, very high thermal and electrical resistance, very good water resistance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 - 1.22 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal method | ||
| Vertical flow direction | 0.50 - 0.70 | % | Internal method |
| Flow direction | 0.30 - 0.50 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 0.060 | % | ISO 62 |
| Saturated, 23°C | 0.14 | % | ISO 62 |
| Water absorption rate- Saturation (100°C) | 0.32 | % | ISO 62 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Reinforcement Content 1(750°C) | 20 | % | ISO 3451 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6400 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 100 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/50 |
| Flexural Modulus 2 | ISO 178 | ||
| 23°C | 6000 | MPa | ISO 178 |
| 60°C | 5200 | MPa | ISO 178 |
| 90°C | 5000 | MPa | ISO 178 |
| Flexural Stress 3 | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | ASTM D256 | ||
| -25°C | 78 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed) | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A50 |
| -- | 138 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Strength | IEC 60243-1 | ||
| 2.00 mm | 23 | kV/mm | IEC 60243-1 |
| 3.00 mm | 17 | kV/mm | IEC 60243-1 |
| Dielectric Constant | 2.90 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | 225 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.970 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 26 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 110 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 260 - 280 | °C | |
| Mold Temperature | 100 - 120 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 100 to 110°CPre-heat Time: 3 hrs |
| Note Message | |
|---|---|
| 1 . | 1 hr |
| 2 . | 1.0 mm/min |
| 3 . | 1.0 mm/min |
| 4 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRIMATOP HDPE 006964 | Amco Polymers | HDPE | PRIMATOP |
| Vitaster® US10NT6182 | Jackdaw Polymers | PBT | Vitaster® |
| Vydyne® R533 NAT | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Altuglas® V 045 I | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| APEX® 90-A481R-65-NT | Teknor Apex Company | PVC, Flexible | APEX® |