Order Products : sales@su-jiao.com
Geon™ Vinyl Rigid Extrusion L6701
| Category: | PVC, Rigid , Rigid Polyvinyl Chloride |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Geon™ Vinyl Rigid Extrusion |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GCWEce_Geon-Vinyl-Rigid-Extrusion-L6701.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Geon L6701 exhibits improved impact properties at lower processing temperatures than Geon 8700X and L6700 products. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.40 | g/cm³ | ASTM D792 |
| PVC Cell Classification | 15344 | ASTM D1784 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D, 15 sec) | 77 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2670 | MPa | ASTM D638 |
| Tensile Strength 2(Yield) | 44.9 | MPa | ASTM D638 |
| Flexural Modulus | 3010 | MPa | ASTM D790 |
| Flexural Strength | 81.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256A | ||
| 23°C, 3.18mm, molded 3 | 150 | J/m | ASTM D256A |
| 23°C, 3.18mm, molded 4 | 650 | J/m | ASTM D256A |
| 23°C, 3.18mm, molded 5 | 460 - 740 | J/m | ASTM D256A |
| Drop Impact Resistance | ASTM D4226 | ||
| 23°C | 71.2 | J/cm | ASTM D4226 |
| 23°C | > 178 | J/cm | ASTM D4226 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, annealed, 3.18mm 6 | 77.8 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm 7 | 75.9 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 8 | 77.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm, molded 9 | 72.2 | °C | ASTM D648 |
| CLTE - Flow | 6.3E-5 | cm/cm/°C | ASTM D696 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Ease of Sizing | Excellent | ||
| Physical properties based on Geon L6701 natural 0000 lot# 4948764 sample unless specified. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 182 - 193 | °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |
| 3 . | Based on commercial production sample extruded profiles. |
| 4 . | Based on commercial production sample milled sheet. |
| 5 . | Obtained from lab scale compound extruded on 2.5" commercial scale machine. |
| 6 . | Annealed at 60 deg.C |
| 7 . | Annealed at 50 deg.C |
| 8 . | Annealed at 60 deg.C |
| 9 . | Annealed at 50 deg.C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYSTONE® P homopolymer | Röchling Engineering Plastics SE & Co. KG | PP Homopolymer | POLYSTONE® |
| RTP 205 TFE 10 SI | RTP Company | Nylon 66 | RTP |
| Vinnolit® E 75 SK | Vinnolit GmbH & Co. KG | PVC Homopolymer | Vinnolit® |
| YUNGSOX® PP 3040C | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| Braskem PP DH357.01 | Braskem Europe GmbH | PP Homopolymer | Braskem PP |