LNP™ LUBRICOMP™ DL0029E compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GBb6H2_LNP-LUBRICOMP-DL0029E-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* DL0029E is a compound based on Polycarbonate resin containing 10% PTFE. Added features of this material include: Wear Resistant, Flame Retardant. Also known as: LNP* LUBRICOMP* Compound DL-4020 FR Product reorder name: DL0029E |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.60 to 0.80 | % | |
| Across Flow : 24 hr | 0.80 to 1.0 | % | |
| Water Absorption (24 hr, 50% RH) | 0.017 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2250 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield 2 | 56.0 | MPa | |
| Break | 51.7 | MPa | |
| Break 3 | 47.0 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield 4 | 5.7 | % | |
| Break | 26 | % | |
| Break 5 | 33 | % | |
| Flexural Modulus | ASTM D790 | ||
| 50.0 mm Span 6 | 2330 | MPa | |
| -- | 2340 | MPa | |
| Flexural Strength | 86.2 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.20 | ||
| vs. Itself - Static | 0.14 | ||
| Wear Factor - Washer | 55.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 2000 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 46.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.20 mm | 141 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 130 | °C | |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.80 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 304 to 316 | °C | |
| Front Temperature | 310 to 321 | °C | |
| Processing (Melt) Temp | 299 to 316 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAMOFIN PPC101 | Polyram Ram-On Industries | PP Copolymer | RAMOFIN |
| RheTech Thermoplastic Polyolefin FT4702-527UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| SUMIPEX® HT55Y | Sumitomo Chemical Co., Ltd. | Acrylic (PMMA) | SUMIPEX® |
| TRIEL® 5752SP | Samyang Corporation | TPEE | TRIEL® |
| Evermore PUR UP-9120NHR | Evermore Chemical Industry Co., Ltd. | PUR-PC | Evermore PUR |