Vyncolit® W5000
| Category: | Phenolic , Phenolic |
| Manufacturer: | Vyncolit N.V. |
| Trademark: | Vyncolit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GB6dL0_Vyncolit-W5000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Vyncolit® W5000 is a glass fiber and mineral filled phenolic molding compound with excellent dimensional stability and a very low coefficient of linear expansion. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.08 | g/cm³ | ISO 1183 |
| Apparent Density | 1.03 | g/cm³ | ISO 60 |
| Molding Shrinkage | 0.15 | % | ISO 2577 |
| Water Absorption (Saturation, 23°C) | 0.060 | % | ISO 62 |
| Post Shrinkage | 0.020 | % | ISO 2577 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Strain at Break | 0.70 | % | ISO 178 |
| Tensile Modulus | 29000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 90.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 0.40 | % | ISO 527-2 |
| Flexural Modulus | 24000 | MPa | ISO 178 |
| Flexural Stress | 180 | MPa | ISO 178 |
| Compressive Stress | 360 | MPa | ISO 604 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 2.8 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 8.5 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 211 | °C | ISO 75-2/Af |
| CLTE | TMA | ||
| Flow | 1.4E-5 | cm/cm/°C | |
| Transverse | 2.5E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILIMIX 59D2 | SILON s.ro | Siloxane, UHMW | SILIMIX |
| Witcom PA66 1L2 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| Ateva® 1241 | Celanese EVA Performance Polymers | EVA | Ateva® |
| Fainplast PVC PM 5525 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Karina NATURAL PVC COMPOUND 900-25/1-AYR-IS (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |