Beetle® PET100 Datasheet,PET,Teknor Apex Company (Chem Polymer)-SHANGHAI SUSHENG

Message
PET100 is an unfilled PET injection moulding grade. It is best suited to thin section amorphous mouldings.

General Information
Features	amorphous
Uses	Thin wall parts
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.34	g/cm³	ISO 1183
Molding Shrinkage ¹	0.50 - 0.70	%	Internal method

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	2500	MPa	ISO 527-2
Tensile Stress (Break)	50.0	MPa	ISO 527-2
Tensile Strain (Break)	> 25	%	ISO 527-2
Flexural Modulus	2500	MPa	ISO 178
Flexural Stress	80.0	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	8.0	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	No Break		ISO 179

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	68.0	°C	ISO 75-2/A

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	1.0E+15	ohms	IEC 60093
Volume Resistivity	1.0E+17	ohms·cm	IEC 60093
Dielectric Strength (3.00 mm)	12	kV/mm	IEC 60243-1
Comparative Tracking Index	225	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm)	HB		Internal method
Glow Wire Flammability Index (1.50 mm)	650	°C	IEC 60695-2-12

Injection	Nominal Value	Unit
Drying Temperature	140	°C
Drying Time	4.0	hr
Rear Temperature	260 - 290	°C
Middle Temperature	260 - 290	°C
Front Temperature	260 - 290	°C
Processing (Melt) Temp	< 280	°C
Mold Temperature	10.0 - 30.0	°C
Injection Rate	Fast
Screw Speed	50 - 200	rpm

Injection instructions
Back pressure: LowInjection pressure: HighPET materials are hygroscopic and very sensitive to moisture content during processing. Unlike many other materials, excessive moisture may not give rise to the appearance of splash marks on the surface of mouldings, but hydrolytic degradation of the melt can lead to significant impairment of properties, characterised most noticeably by embrittlement of the mouldings and reduced melt viscosity. Adequate pre-drying is therefore essential.Drying should ideally be carried out in a vacuum oven or a dehumidified air drier. The recommended drying time for dehumidified air dryers is 4 hours at 140°C. Drying times may need to be extended if the material has become very wet.

Injection instructions

Back pressure: LowInjection pressure: HighPET materials are hygroscopic and very sensitive to moisture content during processing. Unlike many other materials, excessive moisture may not give rise to the appearance of splash marks on the surface of mouldings, but hydrolytic degradation of the melt can lead to significant impairment of properties, characterised most noticeably by embrittlement of the mouldings and reduced melt viscosity. Adequate pre-drying is therefore essential.Drying should ideally be carried out in a vacuum oven or a dehumidified air drier. The recommended drying time for dehumidified air dryers is 4 hours at 140°C. Drying times may need to be extended if the material has become very wet.

Note Message
1 .	Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions. The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Note Message

1 .

Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions. The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding).

Category:	PET , Polyethylene Terephthalate
Manufacturer:	Teknor Apex Company (Chem Polymer)
Trademark:	Beetle®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	GB3taR_Beetle-PET100.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Riblene® GP 26	Versalis S.p.A.	LDPE	Riblene®
Visico™ LE4423/LE4460/ LE4437	Borealis AG	PE, Unspecified	Visico™
ACCUTECH™ HP0334G5M25CL	ACLO Compounders Inc.	PP Homopolymer	ACCUTECH™
Electrafil® 02010 MB	Techmer Engineered Solutions	PP, Unspecified	Electrafil®
INEOS PP 102-CA03	INEOS Olefins & Polymers Europe	PP Homopolymer	INEOS PP