CYCOLOY™ C2950 resin
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | CYCOLOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GAzvxr_CYCOLOY-C2950-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Non-chlorinated and non-brominated flame retardant PC/ABS offering balanced flow and impact plus improved heat resistance intended for various applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 1.18 | g/cm³ | |
| -- 1 | 1.22 | g/cm³ | |
| Melt Mass-Flow Rate (MFR) (260°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Across Flow : 3.20 mm | 0.40 to 0.60 | % | |
| Water Absorption | ASTM D570 | ||
| 24 hr | 0.10 | % | |
| Equilibrium, 23°C | 0.40 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 123 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 62.7 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 40 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 2650 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 160 | J/m | |
| 23°C | 530 | J/m | |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Total Energy | 54.2 | J | |
| 23°C, Total Energy | 61.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 104 | °C | |
| 1.8 MPa, Unannealed, 3.20 mm | 90.6 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 95.0 | °C | |
| Vicat Softening Temperature | 113 | °C | ASTM D1525 6 |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 7.2E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 7.2E-5 | cm/cm/°C | |
| Thermal Conductivity | 0.20 | W/m/K | ASTM C177 |
| RTI Elec | 85.0 | °C | UL 746 |
| RTI Imp | 85.0 | °C | UL 746 |
| RTI Str | 85.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+16 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 19 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 3.00 | ||
| 60 Hz | 3.00 | ||
| 100 Hz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 5.0E-3 | ||
| 60 Hz | 5.0E-3 | ||
| 100 Hz | 4.9E-3 | ||
| Arc Resistance 7 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 0 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 2 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 1 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 2.49 mm | 5VB | ||
| Oxygen Index | 32 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.0 to 88.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.040 | % | |
| Suggested Shot Size | 30 to 80 | % | |
| Rear Temperature | 221 to 254 | °C | |
| Middle Temperature | 221 to 277 | °C | |
| Front Temperature | 243 to 277 | °C | |
| Nozzle Temperature | 243 to 277 | °C | |
| Processing (Melt) Temp | 243 to 277 | °C | |
| Mold Temperature | 60.0 to 82.0 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | Color |
| 2 . | Type I, 50 mm/min |
| 3 . | Type I, 50 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| 7 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiten® 118P | ITEN INDUSTRIES | Phenolic | Resiten® |
| Tritan™ TX1500HF | Eastman Chemical Company | Copolyester | Tritan™ |
| BJB Epoxy TC-1650 A/B | BJB Enterprises, Inc. | Epoxy | BJB Epoxy |
| EQUATE PE EGDA-6888 | EQUATE Petrochemical Company KSCC | HDPE Copolymer | EQUATE PE |
| KOPA® KN133G15HSBL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |