LNP™ LUBRICOMP™ RFL36 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GAxSoH_LNP-LUBRICOMP-RFL36-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP RFL36 is a compound based on Nylon 66 resin containing Glass Fiber, PTFE. Also known as: LNP* LUBRICOMP* Compound RFL4036 Product reorder name: RFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.51 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (275°C/5.0 kg) | 15.0 to 20.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 24 hr | 0.44 | % | |
| Flow : 24 hr | 0.050 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.3 | % | |
| Equilibrium, 23°C, 50% RH | 0.46 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 166 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus 1 | ISO 178 | ||
| -- | 7200 | MPa | |
| 60°C | 5300 | MPa | |
| 100°C | 4200 | MPa | |
| 150°C | 3500 | MPa | |
| 200°C | 3100 | MPa | |
| Flexural Stress 2 | ISO 178 | ||
| -- 3 | 234 | MPa | |
| -- 4 | 277 | MPa | |
| 60°C 5 | 179 | MPa | |
| 100°C 6 | 131 | MPa | |
| 150°C 7 | 96.0 | MPa | |
| 200°C 8 | 83.0 | MPa | |
| Coefficient of Friction (vs. Itself - Dynamic) | 0.59 | ASTM D3702 Modified | |
| Flexural Strain at Break 9 | ISO 178 | ||
| -- | 4.1 | % | |
| 60°C | 6.1 | % | |
| 100°C | 6.6 | % | |
| 150°C | 5.6 | % | |
| 200°C | 6.3 | % | |
| Wear Factor - Washer | 12.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C 10 | 12 | kJ/m² | |
| 23°C 11 | 16 | kJ/m² | |
| Unnotched Izod Impact Strength 12 | ISO 180/1U | ||
| -40°C | 74 | kJ/m² | |
| 23°C | 84 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 13 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | > 220 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | > 220 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 2.5E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.5E-5 | cm/cm/°C | |
| Specific Heat | 1990 | J/kg/°C | ASTM E1269 |
| Thermal Conductivity | 0.25 | W/m/K | ASTM D5930 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Yield |
| 4 . | Break |
| 5 . | Yield |
| 6 . | Yield |
| 7 . | Yield |
| 8 . | Yield |
| 9 . | 2 mm/min |
| 10 . | 80*10*3 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 |
| 13 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Xuchuan 6170/B-8280 (Sole) | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| NEFTEKHIM PP 1552N (YF39S) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Hostacom SD068-4C | LyondellBasell Industries | PP, HMS | Hostacom |
| Lupoy® GN5001EF | LG Chem Ltd. | PC+ABS | Lupoy® |
| POCAN® B 7616 000000 | LANXESS Corporation | PC+PBT | POCAN® |