Polifil® PC GFPC-20
| Category: | PC , Polycarbonate |
| Manufacturer: | The Plastics Group |
| Trademark: | Polifil® PC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GAVvd9_Polifil-PC-GFPC-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polifil® GFPC series compounds offer a combination of improved dimensional stability and decreased flammability. The excellent balance of physical properties make the Polifil® glass-filled polycarbonate line an excellent choice for electrical, appliance, and hardware applications. Standard processing techniques are applicable. Use this information as a guide to aid you in selecting the proper resin for your application. TPG will custom compound and fine-tune our formulations for your application. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.30 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 120 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5870 | MPa | ASTM D638 |
| Tensile Strength (23°C) | 109 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield, 23°C | 3.0 | % | |
| Break, 23°C | 5.0 | % | |
| Flexural Modulus - Tangent (23°C) | 5380 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 131 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Gardner Impact (23°C, 12.7 mm) | 0.452 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 149 | °C | |
| 1.8 MPa, Unannealed | 146 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 to 5.0 | hr | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 271 to 282 | °C | |
| Front Temperature | 277 to 293 | °C | |
| Nozzle Temperature | 282 to 299 | °C | |
| Processing (Melt) Temp | 277 to 304 | °C | |
| Mold Temperature | 76.7 to 98.9 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.172 to 0.517 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PET 40G6F | Asia International Enterprise (Hong Kong) Limited | PET | AIE PET |
| GAPEX® RPP30EB59HB NATURAL | Ferro Corporation | PP Homopolymer | GAPEX® |
| Karina IVORY PVC COMPOUND 90900-35/ 1-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupoy® GP1000MR | LG Chem Ltd. | PC | Lupoy® |
| Osterlene® PPC20-2.7 | Osterman & Company | PP, High Crystal | Osterlene® |