DINALON® B1S25 G30 is a Polyamide 6 (Nylon 6) product filled with 30% glass fiber. It is available in Europe. |
General Information | |
---|---|
Filler / Reinforcement |
|
Appearance |
|
Forms |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Density | 1.37 | g/cm³ | ISO 1183/A |
Humidity 1 | < 0.25 | % | ISO 15512/B |
Mechanical | Nominal Value | Unit | Test Method |
---|---|---|---|
Tensile Modulus | 9500 | MPa | ISO 527-2 |
Tensile Stress (Break) | 190 | MPa | ISO 527-2 |
Tensile Strain (Break) | 3.5 | % | ISO 527-2 |
Flexural Modulus | 9200 | MPa | ISO 178 |
Flexural Stress | 280 | MPa | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
---|---|---|---|
Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
Charpy Unnotched Impact Strength (23°C) | 85 | kJ/m² | ISO 179/1eU |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | 205 | °C | ISO 75-2/A |
Vicat Softening Temperature | > 200 | °C | ISO 306/B |
Note Message | |
---|---|
1 . | Karl-Fischer |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
TEPCON® M90 | Polyplastics Co., Ltd. | Acetal (POM) Copolymer | TEPCON® |
VITAMIDE® AS20WT6432 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
DAI-EL鈩?G-671 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
KumhoSunny ABS HAG5230FR | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
MARPOL® EVA 602 | Marco Polo International, Inc. | EVA | MARPOL® EVA |