Tritan™ MP100
| Category: | Copolyester , Copolyester |
| Manufacturer: | Eastman Chemical Company |
| Trademark: | Tritan™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | GA7uru_Tritan-MP100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Eastman Tritan™ MP100 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Film and sheet manufactured from this new-generation copolyester can be thermoformed with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan™ MP100 copolyester is suitable for use with most forms of sterilization including radiation and ethylene oxide. It is NOT suitable for autoclave/steam sterilization. Eastman Tritan™ MP100 copolyester has been formulated for use in medical film, sheet, and packaging applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.19 | g/cm³ | ASTM D1505 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Taber Abrasion Resistance (23°C) 1 | 23% Haze | ASTM D1044 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Dioxide Permeability (23°C, 250.0 µm) | 150 | cm³·mm/m²/atm/24 hr | ASTM D1434 |
| PPT Tear Resistance | ASTM D2582 | ||
| MD : 23°C, 250.0 µm | 42 | N | |
| TD : 23°C, 250.0 µm | 56 | N | |
| Tear Propagation Resistance | ASTM D1938 | ||
| MD, Split Tear Method : 23°C, 250.0 µm | 410 | gf | |
| TD, Split Tear Method : 23°C, 250.0 µm | 310 | gf |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| UV Transmittance 2 | 89 | % |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Energy - Polar (23°C) | 45 | dyne/cm | ASTM D5946 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 250 | µm | ASTM D374 |
| Elastic Modulus - MD (250 µm) | 1460 | MPa | ASTM D882 |
| Elastic Modulus - TD (250 µm) | 1380 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 250 µm | 41.0 | MPa | |
| TD : Yield, 250 µm | 40.0 | MPa | |
| MD : Break, 250 µm | 59.0 | MPa | |
| TD : Break, 250 µm | 52.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Yield, 250 µm | 7.0 | % | |
| TD : Yield, 250 µm | 7.0 | % | |
| MD : Break, 250 µm | 180 | % | |
| TD : Break, 250 µm | 200 | % | |
| Dart Drop Impact 3 | ASTM D1709A | ||
| -30°C, 250 µm | 910 | g | |
| -18°C, 250 µm | 870 | g | |
| 23°C, 250 µm | 880 | g | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 250 µm | 520 | g | |
| TD : 250 µm | 580 | g | |
| Trouser Tear Resistance 4 | ISO 6383-1 | ||
| MD : 250 µm | 11.0 | N/mm | |
| TD : 250 µm | 11.0 | N/mm | |
| Oxygen Permeability (23°C, 250 µm, 50% RH) | 32 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Water Vapor Transmission Rate | ASTM F1249 | ||
| 23°C, 100% RH, 250 µm | 4.0 | g/m²/24 hr | |
| 38°C, 100% RH, 250 µm | 11 | g/m²/24 hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Instrumented Dart Impact (23°C, Total Energy) | 4.60 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Glass Transition Temperature | 110 | °C | DSC |
| CLTE - Flow (23°C) | 8.8E-5 | cm/cm/°C | ASTM D696 |
| Specific Heat | DSC | ||
| 60°C | 1710 | J/kg/°C | |
| 100°C | 1890 | J/kg/°C | |
| 150°C | 2250 | J/kg/°C | |
| 200°C | 2400 | J/kg/°C | |
| 250°C | 2570 | J/kg/°C |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 250 µm) | 161 | ASTM D2457 | |
| Refractive Index | 1.545 | ASTM D542 | |
| Transmittance (Total, 250 µm) | 92.0 | % | ASTM D1003 |
| Haze (250 µm) | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 25 cycles |
| 2 . | UV/Vis Spectro, 380 nm |
| 3 . | 12.7 mm dia. head, 127 mm dia. clamp, 600 mm drop |
| 4 . | 200 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Network Polymers SBN 150 | Network Polymers, Inc. | SBA | Network Polymers SBN |
| Ferro PP LPP30BF57NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Epic Urethane S7214 | Epic Resins | PUR, Unspecified | Epic Urethane |
| LEXAN™ LGK3020 resin | SABIC Innovative Plastics Asia Pacific | PC | LEXAN™ |
| O'Tech OW 827 | O'Tech Corporation | PVC, Unspecified | O'Tech |